• Type MR3-2 Faraday Rotator Glass Elements

    * Paramagnetism Faraday Rotator Glass Elements 
    Type MR3-2,  faraday rotator glass with higher Verdet constant -0.33 min/Oe-cm at 632.8nm or -96rad/T*m at 632.8 nm
     Type MR4,  faraday rotator glass with highest Verdet constant -0.38 min/Oe-cm at 632.8nm or -110 rad/T*m at 632.8 nm

     

    * Excellent homogeneity
    * Very small stress birefraction
    * High damage threshold
    * Broad wavelength range
    * Better transparency properties
    * Lower nonlinear refractive index
    * Lower absorption coeffcient
    * Lower cost
    * Large dimension available