Specifications︰ The Properties of MR3-2 Faraday Rotator Glass / Magneto Optical Glass
At 20 ℃ temperature
Verdet Constant -0.33min/Oe*cm or -95.7rad/T*m at 632.8 nm
Verdet Constant -0.11 min/Oe-cm or -31.4 rad/T*m at 1064 nm
Transmission window:400nm-1600nm
Refractive indices
ND=1.7441
Nd=1.7442
NF=1.7544
Nc=1.7400
N1064=1.7178
Optical Quality(△n) /cm < 1x10*-6.
Abbe number:
VD=52.50
Vd=51.50
Nonlinear refrective index n2 (x10*-13 e.s.u.)=2.74
Figure of merit V632.8 (nd/n2)=0.62
Density (g/cm*3):4.95
Transformation temperature Tg: 790℃
Sag temperature Ts: 825℃
Coeff.of linear thermal expansion:
0 - 300℃ (10*-7/℃)=62.6
100 - 300℃ (10*-7/℃)=68.2
Transparence rate T% ≥ 86% (Uncoated)
Transparence rate T% ≥ 98% (Coated)
Absorption coefficients < 0.001/cm at 1064nm.
Thermal conductivity=48.10/ ℃(0-100 ℃)
dv/dt=0.0016(0-40 ℃)
dv/dt=0.0006(40-80℃)
Bulk laser damage threshold > 25 (Joules/cm*2) 10 ns pulse width at 1064 nm
Chemical properties (Wt 10ss%)
DW (H2O, 100℃,1 hour )=0.001
DA (0.01N-HNO3,100℃,1 hour)=0.215
* Specifications and information are subject to change without prior notice
Advantages︰ Magneto Optical Glass / Faraday Rotator Glass offer the following advantages
* Highest Verdet constant: -0.24,-0.25,-0.33,-0.38 min/Oe.cm at 633 nm
* Excellent homogeneity
* Very small stress birefraction
* High damage threshold
* Broad wavelength range
* Better transparency properties
* Lower nonlinear refractive index
* Lower absorption coeffcient
* Lower cost
* Large dimension available
Product Description
Faraday Rotator Glass / Magneto Optical Glass
Since glass material in high power laser system is damaged as a consequence of self-focusing,low non-linear refractive index as well as high Verdet constant are important factors for Magneto-Optical Glass
Our world-leading Magneto Optical Glass with very high Verdet factor,we supply them with the shape or size of your choice
Very large plates/disks/rods from diameter 1.00 mm to 300 mm are available
Faraday Rotator Glass / Magnetic Optical Glass mainly used in faraday rotating components,fabricating optics-isolators,faraday rotators,circulators,magneto-optical modulators,optical switchs,interleavers,laser gyroscopes,goniometric devices magneto-optic storage and optical information process system,current measuring transducers for magnetic field measuring and high-voltage transmission line,new generation current sensors,wave guides, iatrology,spaceflight control,satellite survey and other functional devices
Faraday Rotator Glass is made with more advanced technologies,so is performance stabilization,sensitive, and inherently immune to interfere.In comparison with artificial crystal,it is inexpensive and easy to get big size block,it has been made into different types of optical fibers,so it's widely used in many fields
|